(Bi1⁄2Na1⁄2)1-xCaxTiO3 세라믹스의 압전 특성 및 상전이 거동 |
이용현, 조정호1, 김병익1, 최덕균 |
한양대학교 신소재공학과 1요업(세라믹)기술원 |
Piezoelectric Properties and Phase Transition behaviors of (Bi1/2Na1/2)1- xCaxTiO3Ceramics |
Yong-Hyun Lee, Jeong-Ho Cho1, Byung-Ik Kim1, Duck-Kyun Choi |
Department Ceramic Engineering, Hanyang University 1Department of Ceramic Building Materials Research, Korea Institute of Ceramic Engineering and Technology |
|
|
|
ABSTRACT |
$(Bi_{1/2}Na_{1/2})TiO_3$-based ceramics have been intensively studied as lead-free piezoelectric ceramics. In this study, the piezoelectric properties and phase transition behaviors of BNT based solid solution $(Bi_{0.5}Na_{0.5})_{1-x}Ca_xTiO_3$ ($X=0.01{sim}0.25$) were investigated. The morphotropic phase boundary(MPB) zone which BNT is transformed from rhombohedral to cubic structure was appeared by adding $CaTiO_3$ with 0.12 mol by the measurement of permittivity and X-ray diffraction. The behavior which ferroelectric BNT with adding $CaTiO_3$ was changed to antiferroelectric and paraelectric state was confirmed by the measurement ofhysterisis loop and depolarization temperature as a function of temperature. As $CaTiO_3$ concentration was increased, the phase transition temperature was decreased. The piezoelectric properties were highest at 0.01 mol of $CaTiO_3$ concentration. The electromechanical coupling factor($K_t$) and mechanical quality factor($Q_m$) were 42% and 254, respectively. |
Key words:
Lead Free, Piezoelectric$(Bi_{1/2}Na_{1/2})TiO_3$, Phase transition, Ferroelectric |
|
|
|